|Autor:||V. Ney, S. Ye, T. Kammermeier, A. Ney, H. Zhou, J. Fallert, H. Kalt, F.-Y. Lo, A. Melnikov, A. D. Wieck|
|Quelle:||J. Appl. Phys. 104, 083904 (2008)|
ZnO(0001) substrates were ion implanted with 100 keV of Co and 300 keV of Gd at different fluences ranging from 5×1013–1×1015/cm2. The resulting Co:ZnO and Gd:ZnO samples were analyzed with respect to their structural, magnetic, and optical properties. The effect of annealing at 350 °C on the structure and the resulting magnetic and optical properties were investigated as well. For Co:ZnO hardly any changes were observable, neither in the structural nor in the magnetic properties, even though the existence of substitutional Co2+ in the ZnO lattice could be shown by means of low temperature photoluminescence especially for Zn-annealed samples. For the much larger Gd ion the implantation leads to a changed crystal structure, which leads to a ferromagneticlike behavior for higher implantation doses, which could even be enhanced by annealing in vacuum. Ferromagnetic behavior in annealed Gd:ZnO is corroborated by ferromagnetic resonance measurements at low temperatures. The distinct behavior of Gd- and Co-implanted ZnO highlights the importance of defects in the understanding of the magnetic properties in dilute magnetic semiconductors.